Nickel Base Dental Casting Alloys for Crown and Bridge

Our Nickel base dental casting alloys enables to obtain smooth and compact surfaces and reduce the oxide formation. It has a strong resistance to traction and excellent workability. They are perfect economical alternative to Gold & Silver based alloys (precious) without compromising its performance thanks to Willett's mechanical properties and biocompatibility.

This packaging of 1KG is registered and certified in Mainland China.

Please let our sales representative know your packaging preference. We are also able to provide private labeling.

Advantages:

(1). Superior mechanical performance castability.

(2). Corrosion resistance, wear resistance, great flexibility.

Element Composition:

Properties:

Beryllium Free Nickel Base Dental Casting Alloys for Casting

We provide options with our label package or private label.

Massive amount for private labeling and packing will be 25kg per bucket.

Manufacturing by San Xin, patented manufacturer base in China.

Advantages:
-Require simple casting process, hassle free!
Easy and convenient operation.

-Rapid melting rate, perfect liquidity!
Easy to acheive ideal casting product.

-Soft oxide layer, makes polishing easier than ever!

Surface will be shinny within no time!

-Automatic forming compact passivation layer after polishing,
Strong corrosion resistance,excellent biocompatibility, contains zero Bertllium!
Patient's oral healthiness is guaranteed!

Composition:

Properties:

FAQ:

What is the perfect temperature to obtain the best result when casting?

The casting temperature should always maintain 100~150℃ higher than liquidus temperature.

What is the perfect timing to obtain the best result when casting?

While casting Nickel Chrome alloys that don't contain Beryllium, the surface of the melting alloys will appear a layer of shadow. Once the shadow disappears and the edges of the alloy have become rounded (melted until it becomes a sphere shape is not necessary) will be the best timing for casting. Perfect timing for casting Cobalt Chrome alloy is to heat it till the surface membrane perforated and a spark of bright light start to appear.

Cobalt Chrome casting piece is incomplete, what are the causes?

1. Casting ring is not heated evenly: While casting Cobalt alloys, casting ring must heat up gradually and slowly before reaches 300℃. Let it sit in the oven in between 300℃ and 600℃ for 10-30 minutes. Once it heats up to the desired temperature, maintain the same temperature for at least 30 minutes before casting.

2. Casting temperature is below/above alloy's requirement.

3. Strub designed improperly: For example, Strub is too narrow. We strongly recommend the Strub diameter consist of 5mm or more.

4. The amount of alloy is not enough for the casting piece or the centrifugal force of casting pressure is not enough.

5. Casting piece has not avoided the heat center.

Success Dental Company provides dental products from laboratory use to clinical use. The company is based in Hong Kong where is known as the free trade city. Our factory is located in Dongguan. The company was found in the 1970s and has always been the top company among all the competitors. After several years, Success Dental Company has expanded to the different part of China and setting sales point throughout major cities.

Success Dental provides customers with the highest quality available on the market with a most competitive price. From clinic to laboratory materials, tools, and machines.

Under Mr. Henry Lam's leadership, staffs are always believed customers are in their best interest. Thus, Success Dental Co. not only advancing every day but also hunger for satisfaction from customers. These are the reasons why many local and foreign large dental companies and brand customers choose Success Dental Company.